{"id":15006,"date":"2025-03-07T06:11:22","date_gmt":"2025-03-07T06:11:22","guid":{"rendered":"https:\/\/www.epicmicron.com\/?p=15006"},"modified":"2025-03-07T06:11:29","modified_gmt":"2025-03-07T06:11:29","slug":"research-on-the-application-of-ultrafine-barium-sulfate-in-water-based-epoxy-ester-primer","status":"publish","type":"post","link":"https:\/\/www.epicmicron.com\/tr\/research-on-the-application-of-ultrafine-barium-sulfate-in-water-based-epoxy-ester-primer\/","title":{"rendered":"Su Bazl\u0131 Epoksi Ester Astar\u0131nda Ultra \u0130nce Baryum S\u00fclfat\u0131n Uygulanmas\u0131na \u0130li\u015fkin Ara\u015ft\u0131rma"},"content":{"rendered":"

Baryum s\u00fclfat m\u00fckemmel kimyasal eylemsizli\u011fe, y\u00fcksek \u00f6zg\u00fcl a\u011f\u0131rl\u0131\u011fa ve d\u00fc\u015f\u00fck ya\u011f emilimine sahiptir ve bu da onu yayg\u0131n olarak kullan\u0131l\u0131r hale getirir. korozyon \u00f6nleyici<\/a> kaplamalar. Boya filmi iyi asit ve alkali direnci, d\u00fc\u015f\u00fck viskozite ve p\u00fcr\u00fczs\u00fcz yay\u0131lma g\u00f6sterir.<\/p>\n\n\n\n

Ancak inorganik dolgu maddeleri, organik re\u00e7inelerle aray\u00fcz uyumlulu\u011fu sorunlar\u0131 ya\u015fayabilir ve bu da boya filminin son fiziksel ve kimyasal \u00f6zelliklerini etkileyebilir. Uyumlulu\u011fu art\u0131rmak i\u00e7in inorganik dolgu maddeleri genellikle y\u00fczey modifiye edilir.<\/p>\n\n\n\n

\"\"
Ultra ince baryum s\u00fclfat<\/em><\/figcaption><\/figure>\n\n\n\n

Farkl\u0131 y\u00fczey de\u011fi\u015ftiricilerin farkl\u0131 i\u015flevleri oldu\u011fundan, farkl\u0131 sistemler i\u00e7in uygun de\u011fi\u015ftiriciyi se\u00e7mek \u00e7ok \u00f6nemlidir. Boya filminin geleneksel mekanik \u00f6zellikleri, ilk su direnci, tuz p\u00fcsk\u00fcrtme direnci, oda s\u0131cakl\u0131\u011f\u0131nda deiyonize suya diren\u00e7, 0,1 mol\/L s\u00fclf\u00fcrik aside diren\u00e7 ve 0,1 mol\/L sodyum hidroksite diren\u00e7 test edilerek kar\u015f\u0131la\u015ft\u0131rmal\u0131 bir \u00e7al\u0131\u015fma y\u00fcr\u00fct\u00fclm\u00fc\u015ft\u00fcr.<\/p>\n\n\n\n

1. Deneysel s\u00fcre\u00e7<\/h2>\n\n\n\n
\"\"<\/figure>\n\n\n\n

Haz\u0131rl\u0131k S\u00fcreci:<\/strong><\/p>\n\n\n\n

(1) Epoksi ester re\u00e7inesini ve su bazl\u0131 kurutma maddesini s\u0131rayla ekleyin, d\u00fc\u015f\u00fck h\u0131zda 400-600 r\/dk'da kar\u0131\u015ft\u0131r\u0131n. Ard\u0131ndan, n\u00f6tralizat\u00f6r DMEA'y\u0131 ekleyin ve d\u00fc\u015f\u00fck h\u0131zda kar\u0131\u015ft\u0131rmaya devam edin.
(2) Em\u00fclsifikasyon i\u00e7in yava\u015f yava\u015f az miktarda su ekleyin ve em\u00fclsifikasyon s\u00fcrecine ba\u011fl\u0131 olarak h\u0131z\u0131 yakla\u015f\u0131k 1000 dev\/dakikaya ayarlay\u0131n.
(3) Em\u00fclsifikasyondan sonra, da\u011f\u0131t\u0131c\u0131y\u0131 ve k\u00f6p\u00fck \u00f6nleyiciyi s\u0131rayla ekleyin ve e\u015fit da\u011f\u0131l\u0131m\u0131 sa\u011flay\u0131n.
(4) Karbon siyah\u0131 ekleyin, d\u00fc\u015f\u00fck h\u0131zda kar\u0131\u015ft\u0131r\u0131n ve t\u00fcm malzemeler eklendikten sonra kapa\u011f\u0131 kapat\u0131n. Yakla\u015f\u0131k 1200 r\/dk'da da\u011f\u0131t\u0131n, ard\u0131ndan baryum s\u00fclfat ve stronsiyum krom sar\u0131s\u0131 ekleyin. Daha fazla da\u011f\u0131t\u0131m i\u00e7in kalan t\u00fcm bile\u015fenleri eklemeden \u00f6nce da\u011f\u0131tmaya devam edin.
(5) Zirkonyum boncuklar\u0131 1 saat boyunca 3000-3500 dev\/dak h\u0131z\u0131nda \u00f6\u011f\u00fctmeye sokun ve kaz\u0131y\u0131c\u0131 inceli\u011fini buna g\u00f6re ayarlay\u0131n.<\/p>\n\n\n\n

2. Deneysel Sonu\u00e7lar<\/strong><\/h2>\n\n\n\n

2.1 Farkl\u0131 Ultra \u0130nce Baryum S\u00fclfatlar\u0131n Performans Kar\u015f\u0131la\u015ft\u0131rmas\u0131<\/strong><\/h3>\n\n\n\n

Ultra ince baryum s\u00fclfat\u0131n temel fiziksel \u00f6zellikleri a\u015fa\u011f\u0131daki \u015fekilde test edildi: \u0130ngiltere\/T<\/strong><\/p>\n\n\n\n

\"\"<\/figure>\n\n\n\n

\u00a037041-2018<\/strong>\u00a0Standart, sonu\u00e7lar\u0131 Tablo 2'de g\u00f6sterilmi\u015ftir.<\/p>\n\n\n\n

Baryum s\u00fclfat tozunu modifiye etmek i\u00e7in \u00fc\u00e7 farkl\u0131 y\u00fczey de\u011fi\u015ftirici kullan\u0131ld\u0131. Modifiye edilen \u00fcr\u00fcn\u00fcn beyazl\u0131\u011f\u0131, par\u00e7ac\u0131k boyutu ve di\u011fer g\u00f6stergeleri orijinal toza benzer kald\u0131. Ya\u011f emilimi 1 puan azald\u0131, ancak azalma \u00f6nemli de\u011fildi. Bunun nedeni, de\u011fi\u015ftirici olarak kullan\u0131lan ba\u011flay\u0131c\u0131 maddenin tozun ya\u011f emilimini b\u00fcy\u00fck \u00f6l\u00e7\u00fcde etkilememesiydi.<\/p>\n\n\n\n

Tablo 1\u2019deki form\u00fcle g\u00f6re d\u00f6rt tip baryum s\u00fclfat dolgu maddesi haz\u0131rlanarak, su bazl\u0131 epoksi ester astarlardaki uygulama performanslar\u0131 kar\u015f\u0131la\u015ft\u0131r\u0131lm\u0131\u015ft\u0131r.<\/p>\n\n\n\n

2.2 Geleneksel Performans Testi<\/strong><\/h3>\n\n\n\n
\"\"<\/figure>\n\n\n\n

Su bazl\u0131 epoksi ester astar\u0131nda farkl\u0131 maddelerle modifiye edilmi\u015f baryum s\u00fclfat kullan\u0131ld\u0131\u011f\u0131nda, da\u011f\u0131labilirli\u011fi tutarl\u0131 kal\u0131r. Ayn\u0131 \u00f6\u011f\u00fctme s\u00fcresi i\u00e7inde 10 \u00b5m \u00fcr\u00fcn gereksinimini kar\u015f\u0131lar. Bunun nedeni, halihaz\u0131rda en da\u011f\u0131labilir metalik olmayan mineral dolgulardan biri olmas\u0131 ve y\u00fczey modifikasyonu yoluyla daha fazla iyile\u015ftirme i\u00e7in s\u0131n\u0131rl\u0131 alan b\u0131rakmas\u0131d\u0131r.<\/p>\n\n\n\n

Sertlik ve yap\u0131\u015fma a\u00e7\u0131s\u0131ndan, y\u00fczey modifiye edilmi\u015f baryum s\u00fclfat orijinal toza g\u00f6re \u00f6nemli bir geli\u015fme g\u00f6stermez. Farkl\u0131 dolgu maddeleri aras\u0131ndaki sertlik de\u011fi\u015fimi esas olarak Mohs sertliklerine ba\u011fl\u0131d\u0131r, baryum s\u00fclfat 3 olarak derecelendirilmi\u015ftir ve bu orta olarak kabul edilir. Genellikle boya filmi sertli\u011fini art\u0131rmak i\u00e7in kullan\u0131lmad\u0131\u011f\u0131ndan, modifikasyonun bu a\u00e7\u0131dan \u00e7ok az etkisi vard\u0131r.<\/p>\n\n\n\n

Parlakl\u0131k a\u00e7\u0131s\u0131ndan, modifiye edilmi\u015f baryum s\u00fclfat orijinal toza benzer performans g\u00f6sterir. Bunun ba\u015fl\u0131ca nedeni, ya\u011f emiliminin neredeyse de\u011fi\u015fmeden kalmas\u0131 ve bunun sonucunda minimum parlakl\u0131k iyile\u015fmesi olmas\u0131d\u0131r.<\/p>\n\n\n\n

Depolama kararl\u0131l\u0131\u011f\u0131 a\u00e7\u0131s\u0131ndan, titanat ba\u011flay\u0131c\u0131 madde ve epoksi silanla modifiye edilmi\u015f baryum s\u00fclfatta kabala\u015fma g\u00f6r\u00fcl\u00fcrken, orijinal toz ve alkil silanla modifiye edilmi\u015f baryum s\u00fclfatta bu sorun g\u00f6r\u00fclmemektedir.<\/p>\n\n\n\n

2.3 Korozyon \u00d6nleyici Performans Testi<\/strong><\/h3>\n\n\n\n
\"\"<\/figure>\n\n\n\n
\"\"<\/figure>\n\n\n\n
\"\"<\/figure>\n\n\n\n

Orijinal toza k\u0131yasla titanat ba\u011flay\u0131c\u0131 madde ile modifiye edilmi\u015f baryum s\u00fclfat, asit ve su direncinde \u00f6nemli iyile\u015fme g\u00f6stermektedir.<\/p>\n\n\n\n

    \n
  • Asit dayan\u0131kl\u0131l\u0131\u011f\u0131 14 g\u00fcnden 25 g\u00fcne \u00e7\u0131k\u0131yor.<\/li>\n\n\n\n
  • Oda s\u0131cakl\u0131\u011f\u0131nda deiyonize suya kar\u015f\u0131 dayan\u0131kl\u0131l\u0131k 17 g\u00fcnden 32 g\u00fcne \u00e7\u0131kar.<\/li>\n\n\n\n
  • Alkali direnci biraz azal\u0131r.<\/li>\n\n\n\n
  • Ba\u015flang\u0131\u00e7taki su ge\u00e7irmezlik ve tuz p\u00fcsk\u00fcrtme dayan\u0131kl\u0131l\u0131\u011f\u0131 de\u011fi\u015fmeden kal\u0131r.<\/li>\n<\/ul>\n\n\n\n

    Ancak, alkil silan ve epoksi silan ile modifiye edilmi\u015f baryum s\u00fclfat, baz\u0131 \u00f6zelliklerin hafif\u00e7e azalmas\u0131yla birlikte \u00f6nemli bir iyile\u015fme g\u00f6stermez. Bunun nedeni, silan birle\u015ftirme ajanlar\u0131n\u0131n esas olarak mineral y\u00fczeyindeki hidroksil gruplar\u0131yla ba\u011flanan hidroksil gruplar\u0131 olu\u015fturmak i\u00e7in hidrolize dayanmas\u0131d\u0131r. Baryum s\u00fclfat d\u00fc\u015f\u00fck bir hidroksil i\u00e7eri\u011fine sahip oldu\u011fundan, modifikasyon etkisi zay\u0131ft\u0131r.<\/p>\n\n\n\n

    \u00d6te yandan titanat ba\u011flay\u0131c\u0131 ajanlar, alkoksi gruplar\u0131 arac\u0131l\u0131\u011f\u0131yla inorganik dolgu maddesiyle kimyasal bir ba\u011f olu\u015fturarak inorganik-organik ara y\u00fczeyde organik bir aktif monokatman olu\u015fturur. Bu, baryum s\u00fclfat ile organik re\u00e7ineler aras\u0131ndaki uyumlulu\u011fu iyile\u015ftirerek kaplaman\u0131n asit ve su direncini \u00f6nemli \u00f6l\u00e7\u00fcde art\u0131r\u0131r.<\/p>\n\n\n\n

    3. Sonu\u00e7<\/h3>\n\n\n\n

    Baryum s\u00fclfat, y\u00fcksek \u00f6zg\u00fcl a\u011f\u0131rl\u0131k, yo\u011fun par\u00e7ac\u0131klar ve d\u00fc\u015f\u00fck ya\u011f emilimi gibi avantajlar sunar ve iyi da\u011f\u0131labilirlik ve yap\u0131\u015fma ile sonu\u00e7lan\u0131r. Ancak, y\u00fczey modifikasyonu bu \u00f6zelliklerde \u00e7ok az iyile\u015ftirme sa\u011flar.<\/p>\n\n\n\n

    Baryum s\u00fclfat\u0131n Mohs sertli\u011fi 3 oldu\u011fundan, boya filmi sertli\u011fini art\u0131rmak i\u00e7in uygun de\u011fildir. Ayr\u0131ca, d\u00fc\u015f\u00fck hidroksil i\u00e7eri\u011fi nedeniyle, silan ba\u011flama maddeleriyle modifikasyon etkisizdir ve bu da minimum performans art\u0131\u015f\u0131na yol a\u00e7ar.<\/p>\n\n\n\n

    Test edilen modifikasyonlar aras\u0131nda titanat ba\u011flay\u0131c\u0131 ajanlar en iyi sonu\u00e7lar\u0131 elde eder. Epoksi ester astarlarda kullan\u0131ld\u0131\u011f\u0131nda, asit ve su direncini \u00f6nemli \u00f6l\u00e7\u00fcde art\u0131r\u0131r ve bu da onlar\u0131 kaplaman\u0131n dayan\u0131kl\u0131l\u0131\u011f\u0131n\u0131 iyile\u015ftirmek i\u00e7in en etkili se\u00e7im haline getirir.<\/p>\n\n\n\n

    \n